Cannon Balls!
- Thread starter ricky5042
- Start date
Help Support Muzzleloading Forum:
rafterob
62 Cal.
Looks like you've got a lot of balls :grin: H ave fun shooting them.
- Joined
- Jul 26, 2006
- Messages
- 658
- Reaction score
- 49
For a cannon? That lot should last a while.
Your close up is a nice pic but the flaws I can see are hard to figure. One looks like a split due to cold shut or a shrinkage pipe, another as though there were a grain of sand in the mold that the lead couldn't wet.
On the other hand, the ball appears shiny and to have filled the mold out generally so you are likely not too cold in the metal.
My suggestions: fill the mold in a smooth continuous pour, making sure that no slag or grit is involved. A bottom pour pot like the Lee electric pot is helpful, but a good closed-spout ladle like the RCBS lead ladle should work fine too.
If you fluxed the lead with borax, the borax might create those flaws. It isn't right for this job. Use a little piece of candle wax for flux (be aware it bursts into flame, don't put in a lot).
Your close up is a nice pic but the flaws I can see are hard to figure. One looks like a split due to cold shut or a shrinkage pipe, another as though there were a grain of sand in the mold that the lead couldn't wet.
On the other hand, the ball appears shiny and to have filled the mold out generally so you are likely not too cold in the metal.
My suggestions: fill the mold in a smooth continuous pour, making sure that no slag or grit is involved. A bottom pour pot like the Lee electric pot is helpful, but a good closed-spout ladle like the RCBS lead ladle should work fine too.
If you fluxed the lead with borax, the borax might create those flaws. It isn't right for this job. Use a little piece of candle wax for flux (be aware it bursts into flame, don't put in a lot).
Hi ChrisPer
Thanks for the input
At present all I have is a standard soup ladle and even when I flux it, there still looks like there is some crud in the pour!
I do flux and scrap off the crap from the top of the lead!
I am looking into getting an electric pot or an RCBS Lead Dipper.
Rick
Thanks for the input
At present all I have is a standard soup ladle and even when I flux it, there still looks like there is some crud in the pour!
I do flux and scrap off the crap from the top of the lead!
I am looking into getting an electric pot or an RCBS Lead Dipper.
Rick
- Joined
- Jul 26, 2006
- Messages
- 658
- Reaction score
- 49
The ladle will be the reason. I don't have a Lee production pot, just the RCBS ladle, a small stainless saucepan and an LP gas camping stove. The floaters don't present to the pour when you use the nozzle style lead ladle.
But this is minor - let us hear how firing the cannon goes!
But this is minor - let us hear how firing the cannon goes!
Guest
You may want to weigh those one by one. You don't want any voids/air pockets ruining your day.
Col. Batguano
75 Cal.
- Joined
- Feb 10, 2011
- Messages
- 5,039
- Reaction score
- 1,424
close enough.
With artillery, that counts!
With artillery, that counts!
Hi all
Iv re weighed the balls I cast from my jeff tanner mould and here are the results from the 50 I weighed!
Scales are Frankford Arsenal DS-750 Electronic Powder Scale.
The balls are .650"
Highest was 408.0gns
Lowest was 397.5gns
The majority were between 404.0gns to 406.5gns
which I didn't think was to bad
what do you all think?
Regards
Rick
Iv re weighed the balls I cast from my jeff tanner mould and here are the results from the 50 I weighed!
Scales are Frankford Arsenal DS-750 Electronic Powder Scale.
The balls are .650"
Highest was 408.0gns
Lowest was 397.5gns
The majority were between 404.0gns to 406.5gns
which I didn't think was to bad
what do you all think?
Regards
Rick