Cracked sear repair options? Foundry?

[Dusty_Traveler]

I acquired an original rifle with a Golcher lock. The nose of the sear cracked many moons ago, and subsequently its wear pattern with the tumbler became rather cattywompus. It still functions correctly, but it's leaving filings in the mortise.

I sent the lock to Cabin Creek to be repaired/heat treated, and they aren't having any luck finding a sear with geometry that will work, short of scratch making a new one.

Does anyone know of someone/a foundry that would be able to wax cast a few sears in steel? Would this be just as expensive as having CC build one from scratch?

Weld it up, shape it down, heat treat it?

Heat treat it as is, and keep on trucking?

Its a simple commercial lock. No fly, no half cock, nothing complicated (or so I thought).

Your suggestions are welcome

 

[user 34300]

A gunsmith worth his salt can make a new sear out of quality steel. It is not a big job.

Casting lock parts is a shortcut and produces second rate parts. You do not have a master mould so casting is not an option anyway.

 

[SOLANCO]

I would do whatever Brad at Cabin Creek thinks is best.

 

[Felix the Cat]

I have done a few of these by TIG welding, shaping and then case hardening....

 

[rich pierce]

I would file the nose off, make a dovetail and fit in a piece of high carbon steel and braze it in place then file to final shape and polish. Brazing temp is higher than hardening temp. Period gunsmiths did this all the time. Harden and temper and the braze will hold.

 

[Pete G]

Casting is an inexpensive way to make multiple copies. You only need one.