Changing pitch of cast buttplate

[Clark Badgett]

LOL
Ok, Jim - since you're the expert here (not being snarky), please enlighten us. How come we've broken brass parts (I broke a dragoon brass backstrap) and you've never had a problem?

You part wasn’t made from proper gun metal brass most likely.

 

[ChuckJonesWagon]

Put mapp gas on brass that long and it will melt.

I would agree.....if the piece were in fact brass.

If you like I'll send you the broken piece, you can video the heating of the piece with mapp gas for the 5 minutes as I watch the metal do nothing.

 

[Tumbledown]

I would agree.....if the piece were in fact brass.

If you like I'll send you the broken piece, you can video the heating of the piece with mapp gas for the 5 minutes as I watch the metal do nothing.

I believe you about the casting. It was more a warning to others that one can unintentionally melt brass with a torch. Found that out when I was heating the end of a rod and it disappeared.

 

[ChuckJonesWagon]

I believe you about the casting. It was more a warning to others that one can unintentionally melt brass with a torch. Found that out when I was heating the end of a rod and it disappeared.

Experience.....the mistakes we make and then try to forward others to not do the same!!

 

[FlinterNick]

Cracked brass because I tried to bend it without heating it: been there, done that*. Don't do it.

* on my first kit-build project (Traditions Kentucky pistol - cheap metal anyway).

You don’t have to heat up brass to bend it, i bend brass butt plates all the time, you just have to take your time and do it gradually, even if you anneal brass and bend it, it could still crack.

The only time I anneal brass is if I’m trying to rough out a shape or if I’m I’m going to attempt to do a brass weld, brass welds are very complicated.

 

[FlinterNick]

If your brass won’t bend, it’s most likely an alloy closer to (if not actually) bronze.

If your brass has a pale yellow color or a slightly pinkish tone, it’s not proper gun metal brass.

Or it’s got too much zinc, some brass’ today are almost completely made of zinc.

 

[wiscoaster]

Or it’s got too much zinc, some brass’ today are almost completely made of zinc.

The "brass" part I broke by bending was a Traditions kit part. I was hoping @James Kibler would know what that metal is and enlighten us, but has so far not done so.